PA6 wear-resistant nylon added 15% polytetrafluoroethylene (PTFE) modified blend
Click:
PA6 added 15% (PTFE) blending modification,Features:
Good self-lubricating performance,Excellent abrasion resistance.
PA6 wear-resistant nylon added 15% polytetrafluoroethylene (PTFE) modified blend properties table：
| Testing Standards | Data | Unit | |
| Density | ASTM D792 | 1.1 | g/cm3 |
| Shrinkage | ASTM D955 | 1.2-1.4 | In./in |
| Tensile Strength | ASTM D638 | 64.3 | MPa |
| Elongation at break | ASTM D638 | % | |
| Flexural strength | ASTM D790 | 70 | MPa |
| Flexural modulus | ASTM D790 | 2100 | GPa |
| Notched Impact Strength | ASTM D256 | 6 | KJ/m2 |
| Heat distortion temperature | ASTM D648 | 210 | ℃(1.8MPa) |
| Flame retardant performance | UL94 | HB |