Nylon PA6+15% glass fiber reinforced modification
Click:
PA6 glass fiber reinforced 15% modified,
good appearance,
dimensionally stable,
Superior mechanical properties.
Nylon PA6+15% glass fiber reinforced modified physical property table:
| Testing Standards | Data | Unit | |
| Density | ASTM D792 | 1.23 | g/cm3 |
| Shrinkage | ASTM D955 | 1.2-1.4 | In./in |
| Tensile Strength | ASTM D638 | 122 | MPa |
| Elongation at break | ASTM D638 | % | |
| Flexural strength | ASTM D790 | 180 | MPa |
| Flexural modulus | ASTM D790 | 5200 | GPa |
| Notched Impact Strength | ASTM D256 | 11 | KJ/m2 |
| Heat distortion temperature | ASTM D648 | 190 | ℃(1.8MPa) |
| Flame retardant performance | UL94 | HB |